Thin-film transistor substrate manufacturing method and thin-film transistor substrate manufactured with same

ABSTRACT

The present invention provides a TFT substrate manufacturing method and a TFT substrate manufactured with the method. The TFT substrate manufacturing method of the present invention uses a photoresist pattern to serve as a shielding mask to allow a metal layer to be directly oxidized, through the anodic oxidation technology, into a gate insulation layer or a passivation layer, and at the same time, forming electrode patterns of gate or source/drain. The entire operation can be conducted in room temperature and is applicable to a flexible substrate that is not resistant to high temperatures without the involvement of expensive high temperature facility, such as chemical vapor deposition, so as to greatly reduce the operation cost of manufacturing a flexible display device. The TFT substrate manufactured with the present invention shows excellent electrical characteristics and is suitable for a flexible display device.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to the field of display technology, and inparticular to a thin-film transistor (TFT) manufacturing method and aTFT manufactured with the method.

2. The Related Arts

The flexible display technology releases the designs of display devicesfrom being constrained to be planar and allows for diverse outsideconfigurations and designs, and demonstrating the characteristics ofbeing thin and light-weighted and impact resistant, making it fit toapplications for various portable devices, such as mobile phones,personal digital assistants (PDAs), and notebook computers. Displaydevices of this kind is flexible and deformable and is more resistant todamage, allows for mounting to a curved surface, and can be manufacturedas electronic newspapers, television walls, and wearable displays, thosebeing desired by general consumers, demonstrating incredible charming oforganic semiconductors.

In addition, another important factor associated with the development ofthe flexible display devices is that the manufacturing operations can bechanged from sheet-fed batch processing to roll-to-roll manufacturing.This means the manufacturing costs of the display devices can besignificantly reduced. Due to having the same thickness and flexibilityas those of paper sheets, possessing the same message updatability asthat of digital electronic media, being advantageous in respect ofmechanical properties, and exhibiting a cost advantage formanufacturing, it is quite likely that the flexible display devices maytake the position of flat panel displays that are currently dominatingthe market and gain certain business opportunity in an emerging market.

A thin-film transistor liquid crystal display (TFT-LCD) is a liquidcrystal display having liquid crystal pixels each of which is driven byTFTs integrated on a backside thereof, where a scanning process isadopted to arbitrarily control the ON/OFF state of each of thedisplaying spots so as to display messages in a manner of high speed,high brightness, and high contrast. An active matrix organic lightemitting diode (AMOLED) display is, similarly, driven by using TFTs witheach pixel is provided with a TFT having a function of switching, andeach pixel provided with a charge storage capacitor, where an entiresystem of a peripheral driving circuit and a display array is integratedon the same substrate. A difference from the TFT structure of TFT-LCD isthat LCD is driven by an electric voltage, while an AMOLED is driven byan electric current so that brightness thereof is proportional to theelectric current so that in addition to an addressing TFT that performsa switching operation between ON/OFF states, a small driving TFT thathas a reduced ON state resistance to allow for the passage of asufficiently large electric current is also needed. A static randomaccess memory (SRAM) is similarly driven by using a TFT.

In a conventional manufacturing process for the TFTs of the flexibledisplay devices, the operation temperatures, particularly the operationtemperature of plasma enhanced chemical vapor deposition (PECVD), aregenerally relatively high, imposing a severe requirement for temperatureof a substrate. The substrate of a TFT of a flexible display device isgenerally made of organic polymer materials, which are not resistant tohigh temperatures so as to hinder the progress of the flexible displaytechnology.

SUMMARY OF THE INVENTION

An object of the present invention is to provide a thin-film transistor(TFT) substrate manufacturing method, of which the entire manufacturingprocess is conducted in room temperature, making it suitable forflexible display technology and requiring no temperature-resistantflexible substrate and also requiring no high temperature manufacturingfacility such as expensive chemical vapor deposition, so as to greatlyreduce the operation cost for manufacturing a flexible display device.

Another object of the present invention is to provide a TFT substrate,which shows excellent electrical characteristics and is suitable for aflexible display device.

To achieve the above objects, the present invention provides a TFTsubstrate manufacturing method, which comprises the following steps:

(1) providing a backing plate and depositing a first metal layer on thebacking plate;

(2) coating a photoresist layer on the first metal layer and subjectingthe photoresist layer to a patterning operation, such that a firstphotoresist pattern is solely preserved; using the first photoresistpattern as a shielding mask to subject the first metal layer to ananodic oxidization operation, such that a portion of the first metallayer that is not covered by the first photoresist pattern is oxidizedand converted into a first metal oxide, and a portion of the first metallayer that is covered by the first photoresist pattern is not oxidizedand remains metal;

(3) peeling the first photoresist pattern from the first metal layer andcontinuously subjecting the first metal layer to the anodic oxidizationoperation such that a metal surface that was covered by the firstphotoresist pattern is oxidized to form the first metal oxide and aportion of the metal that is located at an under side thereof and notoxidized forms a gate electrode, while the first metal oxide located onthe gate electrode and the backing plate constitutes a gate insulationlayer;

(4) depositing a metal oxide semiconductor material on the gateinsulation layer and conducting a photolithographic operation to form anactive layer;

(5) depositing a second metal layer on the active layer and the gateinsulation layer;

(6) coating a photoresist layer on the second metal layer and subjectingthe photoresist layer to a patterning operation, such that a secondphotoresist pattern is solely preserved; using the second photoresistpattern as a shielding mask to subject the second metal layer to ananodic oxidization operation, such that a portion of the second metallayer that is not covered by the second photoresist pattern is oxidizedand converted into a second metal oxide, and a portion of the secondmetal layer that is covered by the second photoresist pattern is notoxidized and remains metal;

(7) peeling the second metal layer from the second photoresist patternand continuously subjecting the second metal layer to the anodicoxidization operation such that a metal surface that was covered by thesecond photoresist pattern is oxidized to form the second metal oxideand a portion of the metal that is located at an under side thereof andnot oxidized forms a source electrode and a drain electrode, while thesecond metal oxide located on the source electrode, the drain electrode,the active layer, and the gate insulation layer constitutes apassivation layer; and

(8) applying a photolithographic operation to form a via in thepassivation layer to correspond to the drain electrode and thendepositing a transparent conductive film on the passivation layer;applying a photolithographic operation to subject the transparentconductive film to patterning to form a pixel electrode in such a waythat the pixel electrode is connected, through the via, to the drainelectrode.

The first metal layer and the second metal layer are formed of amaterial that comprises at least one of aluminum, magnesium, titanium,an aluminum alloy, a magnesium alloy, and a titanium alloy.

The metal oxide semiconductor material comprises one of ZnO, In₂O₃, andSnO₂ or a combination of multiple ones thereof.

The pixel electrode is formed of a material comprising indium tin oxideor indium zinc oxide.

Step (1) uses physical vapor deposition to deposit the first metallayer; step (4) uses physical vapor deposition to deposit the metaloxide semiconductor material; step (5) uses physical vapor deposition todeposit the second metal layer; and step (8) uses physical vapordeposition to deposit the transparent conductive film.

In steps (2), (3), (6), and (7), in the anodic oxidization operation, acorrosion-resistant conductive material is used as the cathode and aweak acid or weak base solution is used as the electrolyte solution.

In the anodic oxidization operation, graphite or platinum is used as thecathode and citric acid solution or ammonium tartrate solution is usedas the electrolyte solution

The present invention also provides a TFT substrate, which comprises: abacking plate, a gate electrode formed on the backing plate, a gateinsulation layer formed on the gate electrode and the backing plate, anactive layer formed on the gate insulation layer, a source electrode anda drain electrode formed on the active layer and the gate insulationlayer, a passivation layer formed on the source electrode, the drainelectrode, the active layer, and the gate insulation layer, and a pixelelectrode formed on the passivation layer, wherein the gate insulationlayer is formed of a material that is an oxide of a material that makesthe gate electrode and the passivation layer is formed of a materialthat is an oxide of a material that makes the source electrode and thedrain electrode.

The passivation layer comprises a via formed therein to correspond tothe drain electrode and the pixel electrode is connected, through thevia, to the drain electrode.

The gate electrode, the source electrode, and the drain electrode areformed of a material that comprises at least one of aluminum, magnesium,titanium, an aluminum alloy, a magnesium alloy, and a titanium alloy;the active layer is formed of a material comprising a metal oxidesemiconductor material; the pixel electrode is formed of a materialcomprising indium tin oxide or indium zinc oxide.

The present invention further provides a TFT substrate manufacturingmethod, which comprises the following steps:

(1) providing a backing plate and depositing a first metal layer on thebacking plate;

(2) coating a photoresist layer on the first metal layer and subjectingthe photoresist layer to a patterning operation, such that a firstphotoresist pattern is solely preserved; using the first photoresistpattern as a shielding mask to subject the first metal layer to ananodic oxidization operation, such that a portion of the first metallayer that is not covered by the first photoresist pattern is oxidizedand converted into a first metal oxide, and a portion of the first metallayer that is covered by the first photoresist pattern is not oxidizedand remains metal;

(3) peeling the first photoresist pattern from the first metal layer andcontinuously subjecting the first metal layer to the anodic oxidizationoperation such that a metal surface that was covered by the firstphotoresist pattern is oxidized to form the first metal oxide and aportion of the metal that is located at an under side thereof and notoxidized forms a gate electrode, while the first metal oxide located onthe gate electrode and the backing plate constitutes a gate insulationlayer;

(4) depositing a metal oxide semiconductor material on the gateinsulation layer and conducting a photolithographic operation to form anactive layer;

(5) depositing a second metal layer on the active layer and the gateinsulation layer;

(6) coating a photoresist layer on the second metal layer and subjectingthe photoresist layer to a patterning operation, such that a secondphotoresist pattern is solely preserved; using the second photoresistpattern as a shielding mask to subject the second metal layer to ananodic oxidization operation, such that a portion of the second metallayer that is not covered by the second photoresist pattern is oxidizedand converted into a second metal oxide, and a portion of the secondmetal layer that is covered by the second photoresist pattern is notoxidized and remains metal;

(7) peeling the second metal layer from the second photoresist patternand continuously subjecting the second metal layer to the anodicoxidization operation such that a metal surface that was covered by thesecond photoresist pattern is oxidized to form the second metal oxideand a portion of the metal that is located at an under side thereof andnot oxidized forms a source electrode and a drain electrode, while thesecond metal oxide located on the source electrode, the drain electrode,the active layer, and the gate insulation layer constitutes apassivation layer; and

(8) applying a photolithographic operation to form a via in thepassivation layer to correspond to the drain electrode and thendepositing a transparent conductive film on the passivation layer;applying a photolithographic operation to subject the transparentconductive film to patterning to form a pixel electrode in such a waythat the pixel electrode is connected, through the via, to the drainelectrode;

wherein the first metal layer and the second metal layer are formed of amaterial that comprises at least one of aluminum, magnesium, titanium,an aluminum alloy, a magnesium alloy, and a titanium alloy;

wherein the metal oxide semiconductor material comprises one of ZnO,In₂O₃, and SnO₂ or a combination of multiple ones thereof; and

wherein the pixel electrode is formed of a material comprising indiumtin oxide or indium zinc oxide.

The efficacy of the present invention is that the present inventionprovides a TFT substrate manufacturing method and a TFT substratemanufactured with the method. The TFT substrate manufacturing methodaccording to the present invention uses a photoresist pattern to serveas a shielding mask to allow a metal layer to be directly oxidized,through the anodic oxidation technology, into a gate insulation layer ora passivation layer, and at the same time, forming electrode patterns ofgate or source/drain. The entire operation can be conducted in roomtemperature and is applicable to a flexible substrate that is notresistant to high temperatures without the involvement of expensive hightemperature facility, such as chemical vapor deposition, so as togreatly reduce the operation cost of manufacturing a flexible displaydevice. The TFT substrate manufactured with the present invention showsexcellent electrical characteristics and is suitable for a flexibledisplay device.

For better understanding of the features and technical contents of thepresent invention, reference will be made to the following detaileddescription of the present invention and the attached drawings. However,the drawings are provided for the purposes of reference and illustrationand are not intended to impose limitations to the present invention.

BRIEF DESCRIPTION OF THE DRAWINGS

The technical solution, as well as other beneficial advantages, of thepresent invention will become apparent from the following detaileddescription of an embodiment of the present invention, with reference tothe attached drawings.

In the drawings:

FIG. 1 is a schematic view illustrating an operation of anodicoxidation;

FIG. 2 is a schematic view illustrating step 1 of a thin-film transistor(TFT) substrate manufacturing method according to the present invention;

FIG. 3 is a schematic view illustrating step 2 of the TFT substratemanufacturing method according to the present invention;

FIG. 4 is a schematic view illustrating step 3 of the TFT substratemanufacturing method according to the present invention;

FIG. 5 is a schematic view illustrating step 4 of the TFT substratemanufacturing method according to the present invention;

FIG. 6 is a schematic view illustrating step 5 of the TFT substratemanufacturing method according to the present invention;

FIG. 7 is a schematic view illustrating step 6 of the TFT substratemanufacturing method according to the present invention;

FIG. 8 is a schematic view illustrating step 7 of the TFT substratemanufacturing method according to the present invention; and

FIG. 9 is a schematic view illustrating step 8 of the TFT substratemanufacturing method according to the present invention and is also aschematic view illustrating a structure of a TFT substrate according tothe present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

To further expound the technical solution adopted in the presentinvention and the advantages thereof, a detailed description is given toa preferred embodiment of the present invention and the attacheddrawings.

The inventive idea of the present invention is to combine themanufacturing of metal oxide semiconductor (TOS) thin-film transistors(TFTs) with the anodic oxidation technology in order to propose a TFTsubstrate manufacturing method suitable for flexible displaying. Theanodic oxidation technology involves techniques of electrochemicaloxidation of metals or alloys. With the supply of a correspondingelectrolyte liquid and operation conditions, metals and alloys thereof,when acted upon by an externally supplied electrical current, wouldundergo reactions where the anodic metal loses electrons so as to makethe electrolyte solution dissociated and an oxidation reaction occurs toform an oxidation layer on a surface of the anodic metal. According tothe time of oxidation of the anode, a film having a thickness of severalnanometers to several micrometers may be formed.

Referring to FIG. 1, a schematic view is given to illustrate anoperation of anodic oxidation. As shown in FIG. 1, an anode 100 formedof metallic aluminum and a cathode 200 formed of graphite or metallicplatinum are provided. After a constant voltage or constant currentpower source 300 is connected between the anode 100 and the cathode 200,the anode 100 and the cathode 200 are both dipped into an electrolytesolution 40. The electrolyte solution 400 can be a weak acid or weakbase solution, such as citric acid solution and ammonium tartratesolution, whereby with electricity supplied to the anode 100 and thecathode 200, the anode 100 undergoes the electrochemical reaction:2Al+3H₂O→Al₂O₃+6e+6H⁺′ and the cathode 200 undergoes the electrochemicalreaction: 6H₂O+6e→3H₂+60H⁻. As can be seen here, the reaction occurringon the anode 100 is a metal oxidation reaction.

Based on the above-described anodic oxidation technology, the presentinvention is designed to use a photoresist pattern to serve as ashielding mask to allow a metal layer to be directly oxidized, throughthe anodic oxidation technology, into a gate insulation layer or apassivation layer, and at the same time, forming electrode patterns ofgate or source/drain. The entire operation can be conducted in roomtemperature and is applicable to a flexible substrate that is notresistant to high temperatures without the involvement of expensive hightemperature facility, such as chemical vapor deposition, so as togreatly reduce the operation cost of manufacturing a flexible displaydevice.

Referring to FIG. 2-9, firstly, the present invention provides athin-film transistor (TFT) substrate manufacturing method, whichcomprises the following steps:

Step 1: as shown in FIG. 2, providing a backing plate 1 and depositing afirst metal layer 10 on the backing plate 1.

Specifically, the backing plate 1 can be a flexible plate or rigidplate. Further, the flexible plate can be a board made of an organicpolymer material and the rigid plate can be a glass board.

Specifically, the first metal layer 10 is formed of a materialcomprising at least one of aluminum (Al), magnesium (Mg), titanium (Ti),an aluminum alloy, a magnesium alloy, and a titanium alloy.

Specifically, physical vapor deposition (PVD) is used to conduct thedeposition of the first metal layer 10.

Step 2: as shown in FIG. 3, coating a photoresist layer on the firstmetal layer 10 and subjecting the photoresist layer to a patterningoperation, such that a first photoresist pattern 12 is solely preserved;using the first photoresist pattern 12 as a shielding mask to subjectthe first metal layer 10 to an anodic oxidization operation, such that aportion of the first metal layer 10 that is not covered by the firstphotoresist pattern 12 is oxidized and converted into a first metaloxide, and a portion of the first metal layer that is covered by thefirst photoresist pattern 12 is not oxidized and remains metal.

Step 3: as shown in FIG. 4, peeling the first photoresist pattern 12from the first metal layer 10 and continuously subjecting the firstmetal layer 10 to the anodic oxidization operation with oxidation timebeing controlled to have a metal surface that was covered by the firstphotoresist pattern 12 oxidized to form the first metal oxide, such thata portion of the metal that is located at an under side thereof and notoxidized forms a gate electrode 2, while the first metal oxide locatedon the gate electrode 2 and the backing plate 1 constitutes a gateinsulation layer 3.

Step 4: as shown in FIG. 5, depositing a metal oxide semiconductormaterial on the gate insulation layer 3 and conducting aphotolithographic operation to form an active layer 4.

Preferably, the metal oxide semiconductor material comprises one of ZnO,In₂O₃, and SnO₂ or a combination of multiple ones thereof.

Specifically, physical vapor deposition is applied to conduct thedeposition of the metal oxide semiconductor material.

Specifically, the photolithographic operation comprises operations ofcoating photoresist, exposure, development, and etching.

Step 5: as shown in FIG. 6, depositing a second metal layer 50 on theactive layer 4 and the gate insulation layer 3.

Specifically, the second metal layer 50 is formed of a materialcomprising at least one of aluminum (Al), magnesium (Mg), titanium (Ti),an aluminum alloy, a magnesium alloy, and a titanium alloy.

Specifically, physical vapor deposition is used to conduct thedeposition of the second metal layer 50.

Step 6: as shown in FIG. 7, coating a photoresist layer on the secondmetal layer 50 and subjecting the photoresist layer to a patterningoperation, such that a second photoresist pattern 52 is solelypreserved; using the second photoresist pattern 52 as a shielding maskto subject the second metal layer 50 to an anodic oxidization operation,such that a portion of the second metal layer 50 that is not covered bythe second photoresist pattern 52 is oxidized and converted into asecond metal oxide, and a portion of the second metal layer that iscovered by the second photoresist pattern 52 is not oxidized and remainsmetal.

Step 7: as shown in FIG. 8, peeling the second metal layer 50 from thesecond photoresist pattern 52 and continuously subjecting the secondmetal layer 50 to the anodic oxidization operation with oxidation timebeing controlled to have a metal surface that was covered by the secondphotoresist pattern 52 oxidized to form the second metal oxide, suchthat a portion of the metal that is located at an under side thereof andnot oxidized forms a source electrode 51 and a drain electrode 53, whilethe second metal oxide located on the source electrode 51, the drainelectrode 53, the active layer 4, and the gate insulation layer 3constitutes a passivation layer 6.

Specifically, in Step 2, Step 3, Step 6, and Step 7, in the anodicoxidization operation, a corrosion-resistant conductive material, suchas graphite or platinum, is used as the cathode 100; and a weak acid orweak base solution, such as citric acid solution and ammonium tartratesolution, is used as the electrolyte solution 400.

Step 8: as shown in FIG. 9, applying a photolithographic operation toform a via 61 in the passivation layer 6 to correspond to the drainelectrode 53 and then depositing a transparent conductive film on thepassivation layer 6; applying a photolithographic operation to subjectthe transparent conductive film to patterning to form a pixel electrode7 in such a way that the pixel electrode 7 is connected, through the via61, to the drain electrode 53.

Specifically, the pixel electrode 7 is formed of a material comprising atransparent conductive material, such as ITO (indium tin oxide) and IZO(indium zinc oxide).

Specifically, physical vapor deposition is used to conduct thedeposition of the transparent conductive film.

In the above-described TFT substrate manufacturing method, a photoresistpattern is used to serve as a shielding mask to allow a metal layer tobe directly oxidized, through the anodic oxidation technology, into agate insulation layer or a passivation layer, and at the same time,forming electrode patterns of gate or source/drain. The entire operationcan be conducted in room temperature and is applicable to a flexiblesubstrate that is not resistant to high temperatures without theinvolvement of expensive high temperature facility, such as chemicalvapor deposition, so as to greatly reduce the operation cost ofmanufacturing a flexible display device.

Referring to FIG. 9, the present invention also provides a TFTsubstrate, which comprises: a backing plate 1, a gate electrode 2 formedon the backing plate 1, a gate insulation layer 3 formed on the gateelectrode 2 and the backing plate 1, an active layer 4 formed on thegate insulation layer 3, a source electrode 51 and a drain electrode 53formed on the active layer 4 and the gate insulation layer 3, apassivation layer 6 formed on the source electrode 51, the drainelectrode 53, the active layer 4, and the gate insulation layer 3, and apixel electrode 7 formed on the passivation layer 6, wherein the gateinsulation layer 3 is formed of a material that is an oxide of amaterial that makes the gate electrode 2 and the passivation layer 6 isformed of a material that is an oxide of a material that makes thesource electrode 51 and the drain electrode 53.

Specifically, the passivation layer 6 comprises a via 61 formed thereinto correspond to the drain electrode 53 and the pixel electrode 7 isconnected, through the via 61, to the drain electrode 53.

Specifically, the backing plate 1 can be a flexible plate or rigidplate. Further, the flexible plate can be a board made of an organicpolymer material and the rigid plate can be a glass board.

Specifically, the gate electrode 2 is formed of a material comprising atleast one of aluminum (Al), magnesium (Mg), titanium (Ti), an aluminumalloy, a magnesium alloy, and a titanium alloy.

The active layer 4 is formed of a material comprising a metal oxidesemiconductor material, and preferably, the metal oxide semiconductormaterial comprises one of ZnO, In₂O₃, and SnO₂ or a combination ofmultiple ones thereof.

The source electrode 51 and the drain electrode 53 are formed of amaterial comprising at least one of aluminum (Al), magnesium (Mg),titanium (Ti), an aluminum alloy, a magnesium alloy, and a titaniumalloy.

Specifically, the pixel electrode 7 is formed of a material comprising atransparent conductive material, such as ITO (indium tin oxide) and IZO(indium zinc oxide).

In summary, the present invention provides a TFT substrate manufacturingmethod and a TFT substrate manufactured with the method. The TFTsubstrate manufacturing method according to the present invention uses aphotoresist pattern to serve as a shielding mask to allow a metal layerto be directly oxidized, through the anodic oxidation technology, into agate insulation layer or a passivation layer, and at the same time,forming electrode patterns of gate or source/drain. The entire operationcan be conducted in room temperature and is applicable to a flexiblesubstrate that is not resistant to high temperatures without theinvolvement of expensive high temperature facility, such as chemicalvapor deposition, so as to greatly reduce the operation cost ofmanufacturing a flexible display device. The TFT substrate manufacturedwith the present invention shows excellent electrical characteristicsand is suitable for a flexible display device.

Based on the description given above, those having ordinary skills ofthe art may easily contemplate various changes and modifications of thetechnical solution and technical ideas of the present invention and allthese changes and modifications are considered within the protectionscope of right for the present invention.

What is claimed is:
 1. A thin-film transistor (TFT) substratemanufacturing method, comprising the following steps: (1) providing abacking plate and depositing a first metal layer on the backing plate;(2) coating a photoresist layer on the first metal layer and subjectingthe photoresist layer to a patterning operation, such that a firstphotoresist pattern is solely preserved; using the first photoresistpattern as a shielding mask to subject the first metal layer to ananodic oxidization operation, such that a portion of the first metallayer that is not covered by the first photoresist pattern is oxidizedand converted into a first metal oxide, and a portion of the first metallayer that is covered by the first photoresist pattern is not oxidizedand remains metal; (3) peeling the first photoresist pattern from thefirst metal layer and continuously subjecting the first metal layer tothe anodic oxidization operation such that a metal surface that wascovered by the first photoresist pattern is oxidized to form the firstmetal oxide and a portion of the metal that is located at an under sidethereof and not oxidized forms a gate electrode, while the first metaloxide located on the gate electrode and the backing plate constitutes agate insulation layer; (4) depositing a metal oxide semiconductormaterial on the gate insulation layer and conducting a photolithographicoperation to form an active layer; (5) depositing a second metal layeron the active layer and the gate insulation layer; (6) coating aphotoresist layer on the second metal layer and subjecting thephotoresist layer to a patterning operation, such that a secondphotoresist pattern is solely preserved; using the second photoresistpattern as a shielding mask to subject the second metal layer to ananodic oxidization operation, such that a portion of the second metallayer that is not covered by the second photoresist pattern is oxidizedand converted into a second metal oxide, and a portion of the secondmetal layer that is covered by the second photoresist pattern is notoxidized and remains metal; (7) peeling the second metal layer from thesecond photoresist pattern and continuously subjecting the second metallayer to the anodic oxidization operation such that a metal surface thatwas covered by the second photoresist pattern is oxidized to form thesecond metal oxide and a portion of the metal that is located at anunder side thereof and not oxidized forms a source electrode and a drainelectrode, while the second metal oxide located on the source electrode,the drain electrode, the active layer, and the gate insulation layerconstitutes a passivation layer; and (8) applying a photolithographicoperation to form a via in the passivation layer to correspond to thedrain electrode and then depositing a transparent conductive film on thepassivation layer; applying a photolithographic operation to subject thetransparent conductive film to patterning to form a pixel electrode insuch a way that the pixel electrode is connected, through the via, tothe drain electrode.
 2. The TFT substrate manufacturing method asclaimed in claim 1, wherein the first metal layer and the second metallayer are formed of a material that comprises at least one of aluminum,magnesium, titanium, an aluminum alloy, a magnesium alloy, and atitanium alloy.
 3. The TFT substrate manufacturing method as claimed inclaim 1, wherein the metal oxide semiconductor material comprises one ofZnO, In₂O₃, and SnO₂ or a combination of multiple ones thereof.
 4. TheTFT substrate manufacturing method as claimed in claim 1, wherein thepixel electrode is formed of a material comprising indium tin oxide orindium zinc oxide.
 5. The TFT substrate manufacturing method as claimedin claim 1, wherein step (1) uses physical vapor deposition to depositthe first metal layer; step (4) uses physical vapor deposition todeposit the metal oxide semiconductor material; step (5) uses physicalvapor deposition to deposit the second metal layer; and step (8) usesphysical vapor deposition to deposit the transparent conductive film. 6.The TFT substrate manufacturing method as claimed in claim 1, wherein insteps (2), (3), (6), and (7), in the anodic oxidization operation, acorrosion-resistant conductive material is used as the cathode and aweak acid or weak base solution is used as the electrolyte solution. 7.The TFT substrate manufacturing method as claimed in claim 6, wherein inthe anodic oxidization operation, graphite or platinum is used as thecathode and citric acid solution or ammonium tartrate solution is usedas the electrolyte solution.
 8. A thin-film transistor (TFT) substrate,comprising: a backing plate, a gate electrode formed on the backingplate, a gate insulation layer formed on the gate electrode and thebacking plate, an active layer formed on the gate insulation layer, asource electrode and a drain electrode formed on the active layer andthe gate insulation layer, a passivation layer formed on the sourceelectrode, the drain electrode, the active layer, and the gateinsulation layer, and a pixel electrode formed on the passivation layer,wherein the gate insulation layer is formed of a material that is anoxide of a material that makes the gate electrode and the passivationlayer is formed of a material that is an oxide of a material that makesthe source electrode and the drain electrode.
 9. The TFT substrate asclaimed in claim 8, wherein the passivation layer comprises a via formedtherein to correspond to the drain electrode and the pixel electrode isconnected, through the via, to the drain electrode.
 10. The TFTsubstrate as claimed in claim 8, wherein the gate electrode, the sourceelectrode, and the drain electrode are formed of a material thatcomprises at least one of aluminum, magnesium, titanium, an aluminumalloy, a magnesium alloy, and a titanium alloy; the active layer isformed of a material comprising a metal oxide semiconductor material;the pixel electrode is formed of a material comprising indium tin oxideor indium zinc oxide.
 11. A thin-film transistor (TFT) substratemanufacturing method, comprising the following steps: (1) providing abacking plate and depositing a first metal layer on the backing plate;(2) coating a photoresist layer on the first metal layer and subjectingthe photoresist layer to a patterning operation, such that a firstphotoresist pattern is solely preserved; using the first photoresistpattern as a shielding mask to subject the first metal layer to ananodic oxidization operation, such that a portion of the first metallayer that is not covered by the first photoresist pattern is oxidizedand converted into a first metal oxide, and a portion of the first metallayer that is covered by the first photoresist pattern is not oxidizedand remains metal; (3) peeling the first photoresist pattern from thefirst metal layer and continuously subjecting the first metal layer tothe anodic oxidization operation such that a metal surface that wascovered by the first photoresist pattern is oxidized to form the firstmetal oxide and a portion of the metal that is located at an under sidethereof and not oxidized forms a gate electrode, while the first metaloxide located on the gate electrode and the backing plate constitutes agate insulation layer; (4) depositing a metal oxide semiconductormaterial on the gate insulation layer and conducting a photolithographicoperation to form an active layer; (5) depositing a second metal layeron the active layer and the gate insulation layer; (6) coating aphotoresist layer on the second metal layer and subjecting thephotoresist layer to a patterning operation, such that a secondphotoresist pattern is solely preserved; using the second photoresistpattern as a shielding mask to subject the second metal layer to ananodic oxidization operation, such that a portion of the second metallayer that is not covered by the second photoresist pattern is oxidizedand converted into a second metal oxide, and a portion of the secondmetal layer that is covered by the second photoresist pattern is notoxidized and remains metal; (7) peeling the second metal layer from thesecond photoresist pattern and continuously subjecting the second metallayer to the anodic oxidization operation such that a metal surface thatwas covered by the second photoresist pattern is oxidized to form thesecond metal oxide and a portion of the metal that is located at anunder side thereof and not oxidized forms a source electrode and a drainelectrode, while the second metal oxide located on the source electrode,the drain electrode, the active layer, and the gate insulation layerconstitutes a passivation layer; and (8) applying a photolithographicoperation to form a via in the passivation layer to correspond to thedrain electrode and then depositing a transparent conductive film on thepassivation layer; applying a photolithographic operation to subject thetransparent conductive film to patterning to form a pixel electrode insuch a way that the pixel electrode is connected, through the via, tothe drain electrode; wherein the first metal layer and the second metallayer are formed of a material that comprises at least one of aluminum,magnesium, titanium, an aluminum alloy, a magnesium alloy, and atitanium alloy; wherein the metal oxide semiconductor material comprisesone of ZnO, In₂O₃, and SnO₂ or a combination of multiple ones thereof;and wherein the pixel electrode is formed of a material comprisingindium tin oxide or indium zinc oxide.
 12. The TFT substratemanufacturing method as claimed in claim 11, wherein step (1) usesphysical vapor deposition to deposit the first metal layer; step (4)uses physical vapor deposition to deposit the metal oxide semiconductormaterial; step (5) uses physical vapor deposition to deposit the secondmetal layer; and step (8) uses physical vapor deposition to deposit thetransparent conductive film.
 13. The TFT substrate manufacturing methodas claimed in claim 11, wherein in steps (2), (3), (6), and (7), in theanodic oxidization operation, a corrosion-resistant conductive materialis used as the cathode and a weak acid or weak base solution is used asthe electrolyte solution.
 14. The TFT substrate manufacturing method asclaimed in claim 13, wherein in the anodic oxidization operation,graphite or platinum is used as the cathode and citric acid solution orammonium tartrate solution is used as the electrolyte solution.